SABIC Innovative Plastics LNP THERMOCOMP DX06313I PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP DX06313I PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DX06313I is 30% glass fiber reinforced, impact modified polycarbonate resin. High flow and good ductility.
Physical Properties Metric English Comments
Specific Gravity 1.42 g/cc
1.42 g/cc
ASTM D792
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.40 %
0.40 %
ISO 62
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.0050 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 30 g/10 min

@Load 5.00 kg,
Temperature 300 °C
 30 g/10 min

@Load 11.0 lb,
Temperature 572 °F
 ASTM D1238
Melt Index of Compound 22 g/10 min

@Load 5.00 kg,
Temperature 300 °C
 22 g/10 min

@Load 11.0 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 105 MPa
15200 psi
Type I, 5 mm/min; ASTM D638
115 MPa
16700 psi
5 mm/min; ISO 527
Elongation at Break 2.6 %
2.6 %
5 mm/min; ISO 527
2.7 %
2.7 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 7.90 GPa
1150 ksi
5 mm/min; ASTM D638
8.30 GPa
1200 ksi
1 mm/min; ISO 527
Flexural Yield Strength 170 MPa
24700 psi
1.3 mm/min, 50 mm span; ASTM D790
175 MPa
25400 psi
2 mm/min; ISO 178
Flexural Modulus 7.20 GPa
1040 ksi
2 mm/min; ISO 178
7.50 GPa
1090 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.60 J/cm
3.00 ft-lb/in
ASTM D256
1.30 J/cm

@Temperature -30.0 °C
 2.44 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 18.0 kJ/m²
8.57 ft-lb/in²
80*10*3; ISO 180/1A
14.0 kJ/m²

@Temperature -30.0 °C
 6.66 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) 54.0 kJ/m²
25.7 ft-lb/in²
80*10*3; ISO 180/1U
50.0 kJ/m²

@Temperature -30.0 °C
 23.8 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1U
Charpy Impact Unnotched 6.50 J/cm²
30.9 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eU
5.50 J/cm²

@Temperature -30.0 °C
 26.2 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 1.70 J/cm²
8.09 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.50 J/cm²

@Temperature -30.0 °C
 7.14 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 25.0 J

@Temperature 23.0 °C
 18.4 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 22.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 12.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
22.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 12.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 68.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 37.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
68.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 37.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 136 °C
277 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
136 °C

@Thickness 3.20 mm
 277 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 142 °C
288 °F
Rate B/50; ASTM D1525
142 °C
288 °F
Rate B/50; ISO 306
143 °C
289 °F
Rate B/120; ISO 306