SABIC Innovative Plastics LNP THERMOCOMP AB002 ABS

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP AB002 ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* AB002 is a compound based on ABS resin containing 10% Glass Bead.
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
1.12 g/cc
0.0405 lb/in³
ASTM D792
Moisture Absorption 0.220 %
0.220 %
50% RH, 24 hrs; ASTM D570
0.360 %
0.360 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0080 - 0.010 cm/cm

@Time 86400 sec
 0.0080 - 0.010 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 30.0 MPa
4350 psi
5 mm/min; ISO 527
32.0 MPa
4640 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 34.0 MPa
4930 psi
5 mm/min; ISO 527
35.0 MPa
5080 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 24 %
24 %
5 mm/min; ISO 527
29 %
29 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 2.2 %
2.2 %
5 mm/min; ISO 527
2.3 %
2.3 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 2.60 GPa
377 ksi
1 mm/min; ISO 527
2.75 GPa
399 ksi
50 mm/min; ASTM D638
Flexural Strength 60.0 MPa
8700 psi
ISO 178
63.0 MPa
9140 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 64.0 MPa
9280 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
2 mm/min; ISO 178
2.59 GPa
376 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.25 J/cm
2.34 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.57 J/cm
10.4 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 34.0 kJ/m²
16.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 13.0 J

@Temperature 23.0 °C
 9.59 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 87.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 48.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
CTE, linear, Transverse to Flow 89.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 49.4 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 92.0 °C
198 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
93.0 °C

@Thickness 3.20 mm
 199 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 79.0 °C
174 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
81.0 °C

@Thickness 3.20 mm
 178 °F

@Thickness 0.126 in
 unannealed; ASTM D648