SABIC Innovative Plastics LNP Stat-loy K3000 Acetal Copoly

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Stat-loy
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Stat-loy K3000 Acetal Copoly.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Stat-loy* K3000 is a compound based on Acetal Copolymer resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ASTM D 792
1.35 g/cc
0.0488 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 1.8 %

@Time 86400 sec
1.8 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.020 - 0.024 cm/cm

@Time 86400 sec
0.020 - 0.024 in/in

@Time 24.0 hour
ASTM D 955
0.020 - 0.024 cm/cm

@Time 86400 sec
0.020 - 0.024 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.019 - 0.024 cm/cm

@Time 86400 sec
0.019 - 0.024 in/in

@Time 24.0 hour
ASTM D 955
0.019 - 0.024 cm/cm

@Time 86400 sec
0.019 - 0.024 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 32.0 MPa
4640 psi
ASTM D 638
43.0 MPa
6240 psi
ISO 527
Tensile Strength, Yield 48.0 MPa
6960 psi
ASTM D 638
48.0 MPa
6960 psi
ISO 527
Elongation at Break 28.6 %
28.6 %
ISO 527
48 %
48 %
ASTM D 638
Elongation at Yield 12 %
12 %
ASTM D 638
12.1 %
12.1 %
ISO 527
Tensile Modulus 1.82 GPa
264 ksi
50 mm/min; ASTM D 638
1.97 GPa
286 ksi
1 mm/min; ISO 527
Flexural Strength 55.0 MPa
7980 psi
ASTM D 790
63.0 MPa
9140 psi
ISO 178
Flexural Modulus 1.66 GPa
241 ksi
ASTM D 790
1.75 GPa
254 ksi
ISO 178
Izod Impact, Notched 1.17 J/cm

@Temperature 23.0 °C
2.19 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 16.82 J/cm

@Temperature 23.0 °C
31.51 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 130 kJ/m²

@Temperature 23.0 °C
61.9 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 23.0 J

@Temperature 23.0 °C
17.0 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 132 °C
270 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
150 °C

@Thickness 3.20 mm
302 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 76.0 °C
169 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
77.0 °C

@Thickness 3.20 mm
171 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+10 - 1.00e+11 ohm-cm
1.00e+10 - 1.00e+11 ohm-cm
ASTM D 257
Surface Resistance 1.00e+10 - 1.00e+11 ohm
1.00e+10 - 1.00e+11 ohm
ASTM D 257