SABIC Innovative Plastics LNP Stat-kon WX98547 PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Carbon Black Filled
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Stat-kon WX98547 PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Stat-kon* WX98547 is a compound based on Polybutylene Terephalate resin containing Carbon Powder. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ASTM D 792
Linear Mold Shrinkage, Flow 0.0090 cm/cm

@Time 86400 sec
0.0090 in/in

@Time 24.0 hour
ASTM D 955
0.0091 cm/cm

@Time 86400 sec
0.0091 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.010 cm/cm

@Time 86400 sec
0.010 in/in

@Time 24.0 hour
ASTM D 955
0.0103 cm/cm

@Time 86400 sec
0.0103 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
ASTM D 638
Elongation at Break 5.1 %
5.1 %
ASTM D 638
Tensile Modulus 2.28 GPa
331 ksi
50 mm/min; ASTM D 638
Flexural Strength 68.0 MPa
9860 psi
ASTM D 790
Flexural Modulus 2.06 GPa
299 ksi
ASTM D 790
Izod Impact, Notched 0.740 J/cm

@Temperature 23.0 °C
1.39 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 81.0 °C

@Thickness 3.20 mm
178 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Electrical Properties Metric English Comments
Surface Resistance 100 ohm
100 ohm
ASTM D 257