SABIC Innovative Plastics LNP Stat-kon MDM40 PP

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Stat-kon MDM40 PP.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Stat-Kon* MDM40 is a compound based on Polypropylene resin containing Mica and Carbon. Characteristics are Statically Conductive.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ASTM D 792
1.13 g/cc
0.0408 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.060 %
0.060 %
23°C / 50% RH; ISO 62
0.070 %

@Time 86400 sec
0.070 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.010 - 0.030 cm/cm

@Time 86400 sec
0.010 - 0.030 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
0.010 - 0.030 in/in

@Time 24.0 hour
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 5.00 MPa
725 psi
5 mm/min; ISO 527
15.0 MPa
2180 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 18.0 MPa
2610 psi
5 mm/min; ISO 527
22.0 MPa
3190 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 14 %
14 %
5 mm/min; ISO 527
47 %
47 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 4.1 %
4.1 %
5 mm/min; ISO 527
4.7 %
4.7 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 1.69 GPa
245 ksi
1 mm/min; ISO 527
2.49 GPa
361 ksi
50 mm/min; ASTM D 638
Flexural Strength 28.0 MPa
4060 psi
ISO 178
Flexural Yield Strength 31.0 MPa
4500 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 1.65 GPa
239 ksi
1.3 mm/min, 50 mm span; ASTM D 790
1.74 GPa
252 ksi
2 mm/min; ISO 178
Izod Impact, Notched 2.28 J/cm

@Temperature 23.0 °C
4.27 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 13.6 J/cm

@Temperature 23.0 °C
25.5 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 19.0 kJ/m²

@Temperature 23.0 °C
9.04 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 95.0 kJ/m²

@Temperature 23.0 °C
45.2 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 19.0 J
14.0 ft-lb
Multiaxial Impact; ISO 6603
24.0 J

@Temperature 23.0 °C
17.7 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 84.2 µm/m-°C

@Temperature -30.0 - 30.0 °C
46.8 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D 696
CTE, linear, Transverse to Flow 103 µm/m-°C

@Temperature -30.0 - 30.0 °C
57.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 93.0 °C
199 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
95.0 °C

@Thickness 3.20 mm
203 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
51.0 °C

@Thickness 3.20 mm
124 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Electrical Properties Metric English Comments
Surface Resistance 2.0 - 4.0 ohm
2.0 - 4.0 ohm
ASTM D 257