Material Notes:
LNP STAT-KON* EE005 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
1.365 g/cc
0.04931 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.23 %
0.23 %
23°C / 50% RH; ISO 62
0.16 %

@Time 86400 sec
0.16 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ASTM D 955
0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm

@Time 86400 sec
0.0030 - 0.0050 in/in

@Time 24.0 hour
ISO 294
0.0030 - 0.0050 cm/cm

@Time 86400 sec
0.0030 - 0.0050 in/in

@Time 24.0 hour
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 194 MPa
28100 psi
ISO 527
200 MPa
29000 psi
ASTM D 638
Elongation at Break 2.1 %
2.1 %
ISO 527
2.1 %
2.1 %
ASTM D 638
Tensile Modulus 11.7 GPa
1700 ksi
1 mm/min; ISO 527
12.33 GPa
1788 ksi
50 mm/min; ASTM D 638
Flexural Strength 246 MPa
35700 psi
ISO 178
277 MPa
40200 psi
ASTM D 790
Flexural Modulus 14.32 GPa
2077 ksi
ASTM D 790
15.01 GPa
2177 ksi
ISO 178
Izod Impact, Notched 0.530 J/cm

@Temperature 23.0 °C
0.993 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 4.48 J/cm

@Temperature 23.0 °C
8.39 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 29.0 kJ/m²

@Temperature 23.0 °C
13.8 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 7.00 J
5.16 ft-lb
Multiaxial Impact; ISO 6603
10.0 J

@Temperature 23.0 °C
7.38 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 19.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
10.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
19.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
10.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 27.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
15.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
27.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
15.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 206 °C
403 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
207 °C

@Thickness 3.20 mm
405 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Electrical Properties Metric English Comments
Volume Resistivity 100 - 1.00e+6 ohm-cm
100 - 1.00e+6 ohm-cm
ASTM D 257
Surface Resistance 100 ohm - 1e+05
100 ohm - 1e+05
ASTM D 257