SABIC Innovative Plastics LNP Stat-kon EE002ER PEI (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon EE002ER PEI (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* EFP36G is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Easy Molding, Mold Release, Electrically Conductive.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | on tensile bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 144 MPa | 20900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 8.50 GPa | 1230 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 184 MPa | 26700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 8.40 GPa | 1220 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
8.33 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 53.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
29.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1000 ohm - 1e+05 | 1000 ohm - 1e+05 | ASTM D 257 |
Users viewing this material also viewed the following:
- Pyrotek Pyrocast PT-190 Refractory Cast Parts
- Michelman® Michem® Coat 50 AFN Fluorocarbon free, water and grease resistant coating
- Michelman® Michem® Emulsion 47950 Nonionic paraffin emulsion
- H.C. Starck Amperit® 235.091 Calcined Bentonite coated with Nickel-Chromium-Aluminum
- LATI Latilub 66-15T G/30 PA66, 30% Glass Fiber Reinforced, PTFE Filled
- Techmer ES HiFill® ABS E GM15 LE 15% Glass Filled
- Fainplast Compounds Hax™ HFX 505 Crosslinkable HFFR Cable Compound
- Amity Thermosets ATS 1613-R Phenolic Molding Nylon and glass Filler, Compression Molded
- Chang Chun Plastic Longlite PM T359J General Purpose Phenolic Molding Compound
Copyright © lookpolymers.com All Rights Reserved