SABIC Innovative Plastics LNP Stat-kon DEL339XC PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon DEL339XC PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DEL339XC is a compound based on Polycarbonate resin containing Carbon Fiber, PTFE, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D 792 |
| 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.00050 cm/cm @Time 86400 sec |
0.00050 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0044 cm/cm @Time 86400 sec |
0.0044 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 129 MPa | 18700 psi | ASTM D 638 |
| 129 MPa | 18700 psi | ISO 527 | |
| Elongation at Break | 1.8 % | 1.8 % | ISO 527 |
| 2.0 % | 2.0 % | ASTM D 638 | |
| Tensile Modulus | 12.7 GPa | 1840 ksi | 1 mm/min; ISO 527 |
| 14.34 GPa | 2080 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 195 MPa | 28300 psi | ASTM D 790 |
| 200 MPa | 29000 psi | ISO 178 | |
| Flexural Modulus | 11.23 GPa | 1629 ksi | ASTM D 790 |
| 12.4 GPa | 1800 ksi | ISO 178 | |
| Izod Impact, Notched | 0.740 J/cm @Temperature 23.0 °C |
1.39 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.85 J/cm @Temperature 23.0 °C |
9.09 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² @Temperature 23.0 °C |
13.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 12.0 J @Temperature 23.0 °C |
8.85 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 34.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 34.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 39.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 39.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 150 °C @Thickness 3.20 mm |
302 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10 - 1.00e+6 ohm | 10 - 1.00e+6 ohm | ASTM D 257 |