SABIC Innovative Plastics LNP STAT-LOY K3000SZ Acetal Copoly (Asia Pacific)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Stat-loy
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-LOY K3000SZ Acetal Copoly (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Stat-loy* K3000SZ is a compound based on Acetal Copolymer resin containing Anti-Static. Added features of this material include: Antistat.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
ASTM D792
1.33 g/cc
0.0480 lb/in³
ISO 1183
Moisture Absorption 2.20 %
2.20 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.018 cm/cm

@Time 86400 sec
 0.018 in/in

@Time 24.0 hour
 ASTM D955
0.0181 cm/cm

@Time 86400 sec
 0.0181 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.018 cm/cm

@Time 86400 sec
 0.018 in/in

@Time 24.0 hour
 ASTM D955
0.0183 cm/cm

@Time 86400 sec
 0.0183 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 31.0 MPa
4500 psi
ASTM D638
36.0 MPa
5220 psi
ISO 527
Tensile Strength, Yield 41.0 MPa
5950 psi
ASTM D638
42.0 MPa
6090 psi
ISO 527
Elongation at Break 49.3 %
49.3 %
ISO 527
59.5 %
59.5 %
ASTM D638
Elongation at Yield 13.3 %
13.3 %
ISO 527
15.8 %
15.8 %
ASTM D638
Tensile Modulus 1.50 GPa
218 ksi
1 mm/min; ISO 527
1.59 GPa
231 ksi
50 mm/min; ASTM D638
Flexural Strength 40.0 MPa
5800 psi
ISO 178
48.0 MPa
6960 psi
ASTM D790
Flexural Modulus 1.44 GPa
209 ksi
ASTM D790
1.50 GPa
218 ksi
ISO 178
Izod Impact, Notched 1.49 J/cm
2.79 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 15.0 kJ/m²
7.14 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*4; ISO 180/1U
Dart Drop, Total Energy 29.0 J
21.4 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 17.0 J
12.5 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.42
0.42
ASTM D3702 Modified
Coefficient of Friction, Static 0.24
0.24
ASTM D3702 Modified
K (wear) Factor 28.2 x 10-8 mm³/N-M
14.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 130 µm/m-°C

@Temperature -40.0 - 40.0 °C
 72.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
130 µm/m-°C

@Temperature -40.0 - 40.0 °C
 72.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 133 µm/m-°C

@Temperature -40.0 - 40.0 °C
 73.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
133 µm/m-°C

@Temperature -40.0 - 40.0 °C
 73.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 146 °C

@Thickness 3.20 mm
 295 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 67.0 °C

@Thickness 3.20 mm
 153 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 1.00e+9 - 1.00e+11 ohm
1.00e+9 - 1.00e+11 ohm
ASTM D257