SABIC Innovative Plastics LNP STAT-KON ZX08301 PPE (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON ZX08301 PPE (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Stat-Kon* ZX08301 compound is a high heat compounds with ESD safe and low warpage performance suitable for use in Semiconductor Packaging Applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0035 cm/cm @Time 86400 sec |
0.0020 - 0.0035 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0045 cm/cm @Time 86400 sec |
0.0030 - 0.0045 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 162 MPa | 23500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.460 J/cm | 0.862 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
7.78 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 56.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C @Thickness 3.20 mm |
392 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 194 °C @Thickness 3.20 mm |
381 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 550000 - 750000 ohm-cm | 550000 - 750000 ohm-cm | ASTM D257 |
| Surface Resistance | 110000 - 250000 ohm | 110000 - 250000 ohm | ASTM D257 |
| Static Decay | 0.10 sec | 0.10 sec | 5000V to <50V; FTMS101B |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 2010 M Polypropylene
- Polykemi AB POLYfill PPC GK8020 Polypropylene Copolymer, Glass Fiber Reinforced
- Covestro Bayblend® 2753 Polycarbonate + ABS Blend, Automotive (discontinued **)
- Materion Beryllium Copper Alloy 25 Rod and Bar; H (TD04) Temper; over 25.4 to 76 mm (UNS C17200)
- SGL Carbon Group EK 3105 Carbon Graphite
- UBE P7115U Electronic Grade Nylon Copolymer Powder
- Tra-Con Tra-Bond 2101 General Purpose Epoxy Adhesive
- DuPont™ Nomex® N102 Texturized Filament Yarn
Copyright © lookpolymers.com All Rights Reserved