SABIC Innovative Plastics LNP STAT-KON Ultem_UC1200 PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON Ultem_UC1200 PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* Ultem_UC1200 is a 12% carbon fiber reinforced PEI. High modulus with ESD characteristics for high-heat applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0012 - 0.0022 cm/cm @Thickness 3.20 mm |
0.0012 - 0.0022 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 7.5 g/10 min @Load 6.60 kg, Temperature 337 °C |
7.5 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 5.1 % | 5.1 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 5.1 % | 5.1 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 8.13 GPa | 1180 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 193 MPa | 28000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 221 MPa | 32100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 7.83 GPa | 1140 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 8.27 GPa | 1200 ksi | 2.6 mm/min, 100 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.16 J/cm | 7.79 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
8.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 14.4 µm/m-°C @Temperature -20.0 - 150 °C |
8.00 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 32.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 39.6 µm/m-°C @Temperature -20.0 - 150 °C |
22.0 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C @Thickness 3.20 mm |
406 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 214 °C | 417 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.57 mm |
V-0 @Thickness 0.0618 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 400 ohm-cm | 400 ohm-cm | ASTM D257 |
| Surface Resistance | 200000 ohm | 200000 ohm | ASTM D257 |
| Static Decay | 0.010 sec | 0.010 sec | 5000V to <50V; FTMS101B |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | 30 - 60 arcs | 30 - 60 arcs | UL 746A |