Material Notes:
LNP STAT-KON* REL33 is a compound based on Nylon 66 resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant.
Physical Properties Metric English Comments
Specific Gravity 1.29 g/cc
1.29 g/cc
ASTM D792
Density 1.29 g/cc
0.0466 lb/in³
ISO 1183
1.30 g/cc
0.0470 lb/in³
ASTM D792
Moisture Absorption 0.610 %
0.610 %
50% RH, 24 hrs; ASTM D570
0.900 %
0.900 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0030 - 0.0060 cm/cm

@Time 86400 sec
 0.0030 - 0.0060 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0080 - 0.010 cm/cm

@Time 86400 sec
 0.0080 - 0.010 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 164 MPa
23800 psi
5 mm/min; ISO 527
169 MPa
24500 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 164 MPa
23800 psi
5 mm/min; ISO 527
169 MPa
24500 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.4 %
2.4 %
5 mm/min; ISO 527
2.7 %
2.7 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 2.4 %
2.4 %
5 mm/min; ISO 527
2.7 %
2.7 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 11.71 GPa
1698 ksi
1 mm/min; ISO 527
12.52 GPa
1816 ksi
50 mm/min; ASTM D638
Flexural Strength 231 MPa
33500 psi
ISO 178
237 MPa
34400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 237 MPa
34400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 8.58 GPa
1240 ksi
2 mm/min; ISO 178
8.73 GPa
1270 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.580 J/cm
1.09 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.32 J/cm
13.7 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 44.0 kJ/m²
20.9 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 7.00 J

@Temperature 23.0 °C
 5.16 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 2.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
 1.11 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
CTE, linear, Transverse to Flow 9.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
 5.00 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
261 °C

@Thickness 3.20 mm
 502 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 244 °C
471 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
253 °C

@Thickness 3.20 mm
 487 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 1.0 - 4.0 ohm
1.0 - 4.0 ohm
ASTM D257