SABIC Innovative Plastics LNP STAT-KON REF42I PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON REF42I PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* REF42I is a compound based on Nylon 6/6 containing Proprietary Fillers. Added feature of this grade is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.690 % | 0.690 % | 50% RH, 24 hrs; ASTM D570 |
| 0.960 % | 0.960 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 176 MPa | 25500 psi | 5 mm/min; ISO 527 |
| 197 MPa | 28600 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 195 MPa | 28300 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 |
| 2.7 % | 2.7 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.6 % | 2.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 13.87 GPa | 2012 ksi | 1 mm/min; ISO 527 |
| 14.66 GPa | 2126 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 264 MPa | 38300 psi | ISO 178 |
| 274 MPa | 39700 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 277 MPa | 40200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 11.5 GPa | 1670 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.43 J/cm | 2.68 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.98 J/cm | 18.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 62.0 kJ/m² | 29.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 22.0 J @Temperature 23.0 °C |
16.2 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
8.89 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 94.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
52.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 261 °C @Thickness 3.20 mm |
502 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.0 - 4.0 ohm | 1.0 - 4.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH T15010 H VTUV1 Polypropylene Homopolymer, Mineral Reinforced
- 3M Dyneon™ TF 2072 PTFE (discontinued **)
- I. Stern 550 High Impact Polystyrene
- ICO Polymers ICORENEâ„¢ 115-1654 LMDPE Rotational Molding Resin
- Techmer ES HiFill FR® PA4/6 GF15 FR HS L 15% Glass Filled (Conditioned)
- Covestro Apec® HT KU 1-9361 High-Heat Polycarbonate
- Eliokem Sunigum® P7395 Acrylate Terpolymer
- AK Steel ZINCGRIP® GA Hot Dip Galvannealed Carbon Steel, Dent Resistant (DR 180)
- PolyOne Synprene® ST-6120 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved