SABIC Innovative Plastics LNP STAT-KON RD000I PA 66 (Asia Pacific)

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP STAT-KON
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP STAT-KON RD000I PA 66 (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* STAT-KON* RD000I is a compound based on Nylon 66 resin containing Carbon Powder, Impact Modifier. Added features of this material include: Electrically Conductive, High Impact.

Physical Properties	Metric	English	Comments
Density	1.15 g/cc	0.0415 lb/inÂ³	ASTM D792

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	46.0 MPa	6670 psi	ASTM D638
Elongation at Break	13.5 %	13.5 %	ASTM D638
Tensile Modulus	2.38 GPa	345 ksi	50 mm/min; ASTM D638
Flexural Strength	82.0 MPa	11900 psi	ASTM D790
Flexural Modulus	2.62 GPa	380 ksi	ASTM D790
Izod Impact, Notched	2.50 J/cm	4.68 ft-lb/in	ASTM D256
Izod Impact, Unnotched	21.89 J/cm	41.01 ft-lb/in	ASTM D4812

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	121 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	67.2 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
Thermal Conductivity	2.80 W/m-K	19.4 BTU-in/hr-ftÂ²-Â°F	ASTM E 1530
Deflection Temperature at 1.8 MPa (264 psi)	75.0 Â°C @Thickness 3.20 mm	167 Â°F @Thickness 0.126 in	unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Surface Resistance	1.0 - 6.0 ohm	1.0 - 6.0 ohm	ASTM D257