Material Notes:

LNP* STAT-KON* OEL36A is a compound based on PPS - Branched resin containing 15% PTFE, 30% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive.

Physical Properties	Metric	English	Comments
Specific Gravity	1.54 g/cc	1.54 g/cc	ASTM D792
Density	1.54 g/cc	0.0556 lb/inÂ³	ISO 1183
Moisture Absorption	0.0200 %	0.0200 %	50% RH, 24 hrs; ASTM D570
	0.0300 %	0.0300 %	23Â°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.00050 - 0.00070 cm/cm @Time 86400 sec	0.00050 - 0.00070 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.0050 - 0.0070 cm/cm @Time 86400 sec	0.0050 - 0.0070 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	168 MPa	24400 psi	5 mm/min; ISO 527
	172 MPa	24900 psi	Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield	170 MPa	24700 psi	Type I, 5 mm/min; ASTM D638
Elongation at Break	0.90 %	0.90 %	Type I, 5 mm/min; ASTM D638
	0.90 %	0.90 %	5 mm/min; ISO 527
Tensile Modulus	25.16 GPa	3649 ksi	1 mm/min; ISO 527
	26.62 GPa	3861 ksi	50 mm/min; ASTM D638
Flexural Strength	225 MPa	32600 psi	1.3 mm/min, 50 mm span; ASTM D790
	258 MPa	37400 psi	ISO 178
Flexural Modulus	20.7 GPa	3000 ksi	1.3 mm/min, 50 mm span; ASTM D790
	21.62 GPa	3136 ksi	2 mm/min; ISO 178
Izod Impact, Notched	0.410 J/cm	0.768 ft-lb/in	ASTM D256
Izod Impact, Unnotched	3.99 J/cm	7.47 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	5.00 kJ/mÂ²	2.38 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	22.0 kJ/mÂ²	10.5 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	5.00 J @Temperature 23.0 Â°C	3.69 ft-lb @Temperature 73.4 Â°F	ASTM D3763
Impact Test	2.00 J	1.48 ft-lb	Multiaxial Impact; ISO 6603

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	8.24 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	4.58 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	ASTM D696
CTE, linear, Transverse to Flow	41.3 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	22.9 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	277 Â°C	531 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	277 Â°C @Thickness 3.20 mm	531 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	262 Â°C	504 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	263 Â°C @Thickness 3.20 mm	505 Â°F @Thickness 0.126 in	unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Surface Resistance	1.0 - 3.0 ohm	1.0 - 3.0 ohm	ASTM D257