SABIC Innovative Plastics LNP STAT-KON Noryl_FMC3008A PPE+PS

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON Noryl_FMC3008A PPE+PS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Stat-kon* Noryl_FMC3008A compound is a 30% carbon fiber/glass/mineral filled, static dissipative, foamable resin. UL94 V1 rated. Property values at 20% weight reduction, 0.250"" wall.
Physical Properties Metric English Comments
Specific Gravity 1.02 g/cc
1.02 g/cc
foam molded; ASTM D792
1.28 g/cc
1.28 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0015 - 0.0025 cm/cm

@Thickness 3.20 mm
 0.0015 - 0.0025 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0015 - 0.0035 cm/cm

@Thickness 3.20 mm
 0.0015 - 0.0035 in/in

@Thickness 0.126 in
 SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 48.0 MPa

@Thickness 6.35 mm
 6960 psi

@Thickness 0.250 in
 ASTM D638
Elongation at Break 3.5 %

@Thickness 6.35 mm
 3.5 %

@Thickness 0.250 in
 ASTM D638
Flexural Yield Strength 102 MPa
14800 psi
6.4 mm; ASTM D790
Flexural Modulus 7.79 GPa
1130 ksi
6.4 mm; ASTM D790
Izod Impact, Unnotched 1.01 J/cm

@Thickness 6.40 mm
 1.89 ft-lb/in

@Thickness 0.252 in
 ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 116 °C

@Thickness 6.40 mm
 241 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 108 °C

@Thickness 6.40 mm
 226 °F

@Thickness 0.252 in
 unannealed; ASTM D648
UL RTI, Electrical 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746B
Flammability, UL94 V-0

@Thickness 3.98 mm
 V-0

@Thickness 0.157 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity 10000 ohm-cm
10000 ohm-cm
ASTM D257
Surface Resistance 1e+05
1e+05
ASTM D257
Descriptive Properties Value Comments
FOAM - ELECTRICAL 6.4 mm Wt Reduction 20%
FOAM - Flame Class Minimum Density 1.15g/cm^3
FOAM - IMPACT 6.4 mm Wt Reduction 20%
FOAM - MECHANICAL 6.4 mm Wt Reduction 20%
FOAM - PHYSICAL 6.4mm Wt Reduction 20%
FOAM - THERMAL 6.4mm Wt Reduction 20%