SABIC Innovative Plastics LNP STAT-KON ME006 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON ME006 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* ME006 is a compound based on Polypropylene resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ASTM D792 |
| 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0300 % | 0.0300 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 |
| 57.0 MPa | 8270 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | 5 mm/min; ISO 527 |
| 58.0 MPa | 8410 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 0.40 % | 0.40 % | 5 mm/min; ISO 527 |
| 0.50 % | 0.50 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 0.40 % | 0.40 % | 5 mm/min; ISO 527 |
| 0.50 % | 0.50 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 13.99 GPa | 2029 ksi | 1 mm/min; ISO 527 |
| 17.34 GPa | 2515 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
| Flexural Yield Strength | 78.0 MPa | 11300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 12.3 GPa | 1780 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 12.33 GPa | 1788 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.410 J/cm | 0.768 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 0.820 J/cm | 1.54 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.3 µm/m-°C @Temperature -30.0 - 30.0 °C |
12.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 59.1 µm/m-°C @Temperature -30.0 - 30.0 °C |
32.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 153 °C @Thickness 3.20 mm |
307 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.0 - 3.0 ohm | 1.0 - 3.0 ohm | ASTM D257 |