SABIC Innovative Plastics LNP STAT-KON EX11318C PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON EX11318C PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-Kon* EX11318C is a polyetherimide compound reinforced with carbon fiber for good stiffness, dimension stability and has extremely high level of cleanliness for the most demanding application. A unique feature of this material is its low C18-C40 hydrocarbons. This compound is manufactured using LNP CCS Technology.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm @Time 86400 sec |
0.0010 - 0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0015 - 0.0025 cm/cm @Time 86400 sec |
0.0015 - 0.0025 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 211 MPa | 30600 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 1.9 % | 1.9 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 21.77 GPa | 3157 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 270 MPa | 39200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 18.14 GPa | 2631 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.75 J/cm | 7.03 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 4.60 µm/m-°C @Temperature -40.0 - 40.0 °C |
2.56 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 43.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C @Thickness 6.40 mm |
397 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5000 - 5.00e+6 ohm-cm | 5000 - 5.00e+6 ohm-cm | ASTM D257 |
| Surface Resistance | 5000 - 500000 ohm | 5000 - 500000 ohm | ASTM D257 |
| Static Decay | 0.10 sec | 0.10 sec | 5000V to <50V; FTMS101B |