SABIC Innovative Plastics LNP STAT-KON EX07311P PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON EX07311P PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP Stat-kon* EX07311P is an easy flowing ESD-safe compound based on Polyetherimide resin. This compound is developed for good dimensional stability for use in ESD Tray for Backend Semicon and HDD tray applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792 |
| 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0029 cm/cm | 0.0029 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0036 cm/cm | 0.0036 in/in | SABIC Method |
| Melt Index of Compound | 30 g/10 min @Load 10.0 kg, Temperature 345 °C |
30 g/10 min @Load 22.0 lb, Temperature 653 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 174 MPa | 25200 psi | 5 mm/min; ISO 527 |
| 175 MPa | 25400 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.7 % | 1.7 % | Flexural Strain, break, 2 mm/min; ISO 178 |
| 1.9 % | 1.9 % | 5 mm/min; ISO 527 | |
| 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 15.0 GPa | 2180 ksi | 5 mm/min; ASTM D638 |
| 15.2 GPa | 2200 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 200 MPa | 29000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 203 MPa | 29400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 11.5 GPa | 1670 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 13.2 GPa | 1910 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.560 J/cm | 1.05 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Coefficient of Friction, Dynamic | 0.40 | 0.40 | ASTM D3702 Modified |
| K (wear) Factor | 40.3 x 10-8 mm³/N-M | 20.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 8.90 µm/m-°C @Temperature -40.0 - 40.0 °C |
4.94 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 43.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 202 °C @Thickness 3.20 mm |
396 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1e+05 - 1.00e+6 ohm-cm | 1e+05 - 1.00e+6 ohm-cm | ASTM D257 |
| Surface Resistance | 1e+05 - 1.00e+6 ohm | 1e+05 - 1.00e+6 ohm | ASTM D257 |
| 1e+05 - 1.00e+6 ohm | 1e+05 - 1.00e+6 ohm | ROA; IEC 60093 |