SABIC Innovative Plastics LNP STAT-KON EE005E PEI

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON EE005E PEI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP STAT-KON* EE005E is a compound based on Polyetherimide resin containing 25% Carbon Fiber. Added features of this material include: Easy Molding, Electrically Conductive.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
1.365 g/cc
0.04931 lb/in³
ASTM D792
Moisture Absorption 0.160 %
0.160 %
50% RH, 24 hrs; ASTM D570
0.230 %
0.230 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.00050 - 0.0030 cm/cm

@Time 86400 sec
0.00050 - 0.0030 in/in

@Time 24.0 hour
ASTM D955
0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm

@Time 86400 sec
0.0030 - 0.0050 in/in

@Time 24.0 hour
ASTM D955
0.0030 - 0.0050 cm/cm

@Time 86400 sec
0.0030 - 0.0050 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 194 MPa
28100 psi
ISO 527
200 MPa
29000 psi
ASTM D638
Elongation at Break 2.1 %
2.1 %
ASTM D638
2.1 %
2.1 %
ISO 527
Tensile Modulus 11.7 GPa
1700 ksi
1 mm/min; ISO 527
12.33 GPa
1788 ksi
50 mm/min; ASTM D638
Flexural Strength 276 MPa
40000 psi
ISO 178
277 MPa
40200 psi
ASTM D790
Flexural Modulus 14.32 GPa
2077 ksi
ASTM D790
15.01 GPa
2177 ksi
ISO 178
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.48 J/cm
8.39 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 29.0 kJ/m²
13.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 10.0 J
7.38 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 7.00 J
5.16 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 19.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
10.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
19.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
10.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 27.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
15.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
27.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
15.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
207 °C

@Thickness 3.20 mm
405 °F

@Thickness 0.126 in
unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 100 - 1.00e+6 ohm-cm
100 - 1.00e+6 ohm-cm
ASTM D257
Surface Resistance 100 ohm - 1e+05
100 ohm - 1e+05
ASTM D257