SABIC Innovative Plastics LNP STAT-KON DX99873C PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DX99873C PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DX99872C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00050 cm/cm @Time 86400 sec |
0.00050 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 99.0 MPa | 14400 psi | ISO 527 |
| 104 MPa | 15100 psi | ASTM D638 | |
| Elongation at Break | 1.6 % | 1.6 % | ISO 527 |
| 1.7 % | 1.7 % | ASTM D638 | |
| Tensile Modulus | 10.75 GPa | 1559 ksi | 50 mm/min; ASTM D638 |
| 10.8 GPa | 1570 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 163 MPa | 23600 psi | ISO 178 |
| 171 MPa | 24800 psi | ASTM D790 | |
| Flexural Modulus | 9.25 GPa | 1340 ksi | ISO 178 |
| 9.68 GPa | 1400 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.85 J/cm | 9.09 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 25.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 37.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 37.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Multibase TPSiV™ 1180-50D Thermoplastic Silicone Vulcanizate
- Protective Coating PC-Concrete™ Epoxy Concrete Anchoring and Repair System
- Polymer Resources AC-G10 Acetal Copolymer, 10% Glass Reinforced
- Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours
- Styron CALIBREâ„¢ 303V-10 Polycarbonate Resin
- Teknor Apex Chemlon® 233 GI Nylon 6, 33% Glass Fiber Reinforced
- ExxonMobil HDPE HD 8660.29 High Density Polyethylene Resin
- Aaron Industries AAROPRENE® AEPC 5000-1 Engineered Polycarbonate Resin
- 3M Scotch® 222 High-temperature Fine Line Masking Tape
- Zhejiang Juner PC-A1-11 Top-Grade Flame Retardant UV-Resistant
Copyright © lookpolymers.com All Rights Reserved