- HOME
- POLYMER SEARCH
- Thermoplastic
- Polycarbonate (PC)
- SABIC Innovative Plastics LNP STAT-KON DX96717C PC
SABIC Innovative Plastics LNP STAT-KON DX96717C PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DX96717C PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DX96717C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.170 % | 0.170 % | 50% RH, 24 hrs; ASTM D570 |
| 0.250 % | 0.250 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0075 cm/cm @Time 86400 sec |
0.0075 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0075 cm/cm @Time 86400 sec |
0.0075 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 51.0 MPa | 7400 psi | ISO 527 |
| 54.0 MPa | 7830 psi | ASTM D638 | |
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | ISO 527 |
| 63.0 MPa | 9140 psi | ASTM D638 | |
| Elongation at Break | 9.9 % | 9.9 % | ASTM D638 |
| 11.1 % | 11.1 % | ISO 527 | |
| Elongation at Yield | 4.7 % | 4.7 % | ISO 527 |
| 5.0 % | 5.0 % | ASTM D638 | |
| Tensile Modulus | 2.48 GPa | 360 ksi | 50 mm/min; ASTM D638 |
| 2.70 GPa | 392 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 98.0 MPa | 14200 psi | ASTM D790 |
| 98.0 MPa | 14200 psi | ISO 178 | |
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO 178 |
| 2.89 GPa | 419 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 18.31 J/cm | 34.30 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 123 kJ/m² | 58.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 27.0 J | 19.9 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C @Thickness 3.20 mm |
289 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 131 °C @Thickness 3.20 mm |
268 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.80 mm |
V-0 @Thickness 0.0709 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10000 - 1.00e+8 ohm | 10000 - 1.00e+8 ohm | ASTM D257 |
Users viewing this material also viewed the following: