SABIC Innovative Plastics LNP STAT-KON DX91077 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DX91077 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* DX91077 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Impact Modified.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.140 % | 0.140 % | 50% RH, 24 hrs; ASTM D570 |
| 0.240 % | 0.240 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | Type I, 5 mm/min; ASTM D638 |
| 48.0 MPa | 6960 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 |
| 56.0 MPa | 8120 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 12.4 % | 12.4 % | 5 mm/min; ISO 527 |
| 15 % | 15 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 4.8 % | 4.8 % | Type I, 5 mm/min; ASTM D638 |
| 4.8 % | 4.8 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1 mm/min; ISO 527 |
| 2.71 GPa | 393 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
| Flexural Yield Strength | 94.0 MPa | 13600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.58 GPa | 374 ksi | 2 mm/min; ISO 178 |
| 2.76 GPa | 400 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 17.4 J/cm | 32.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 125 kJ/m² | 59.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 31.0 J @Temperature 23.0 °C |
22.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 28.0 J | 20.7 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.8 µm/m-°C @Temperature -30.0 - 30.0 °C |
36.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 67.1 µm/m-°C @Temperature -30.0 - 30.0 °C |
37.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 139 °C @Thickness 3.20 mm |
282 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 4.0 - 6.0 ohm | 4.0 - 6.0 ohm | ASTM D257 |