SABIC Innovative Plastics LNP STAT-KON DX12411C PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DX12411C PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* DX12411C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Density | 1.246 g/cc | 0.04501 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| 0.220 % | 0.220 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0085 cm/cm @Time 86400 sec |
0.0085 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 5 mm/min; ASTM D638 |
| 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | 5 mm/min; ISO 527 |
| 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 12.3 % | 12.3 % | 5 mm/min; ISO 527 |
| 19 % | 19 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 4.6 % | 4.6 % | 5 mm/min; ISO 527 |
| 4.7 % | 4.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.56 GPa | 371 ksi | 1 mm/min; ISO 527 |
| 2.63 GPa | 381 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 88.0 MPa | 12800 psi | ISO 178 |
| Flexural Modulus | 2.54 GPa | 368 ksi | 2 mm/min; ISO 178 |
| 2.69 GPa | 390 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 2.96 J/cm | 5.55 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1A |
| Dart Drop, Total Energy | 34.0 J @Temperature 23.0 °C |
25.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 33.0 J | 24.3 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 71.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
39.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
40.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 139 °C @Thickness 3.20 mm |
282 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C | 225 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 - 1.00e+6 ohm-cm | 1000 - 1.00e+6 ohm-cm | ASTM D257 |
| Surface Resistance | 1000 - 1.00e+6 ohm | 1000 - 1.00e+6 ohm | ASTM D257 |