- SABIC Innovative Plastics LNP STAT-KON DX05499 PC (Asia Pacific)
SABIC Innovative Plastics LNP STAT-KON DX05499 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DX05499 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DX05499 is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.110 % | 0.110 % | 50% RH, 24 hrs; ASTM D570 |
| 0.190 % | 0.190 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0064 cm/cm @Time 86400 sec |
0.0064 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0066 cm/cm @Time 86400 sec |
0.0066 in/in @Time 24.0 hour |
ISO 294 |
| 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ISO 527 |
| 60.0 MPa | 8700 psi | ASTM D638 | |
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | ISO 527 |
| 67.0 MPa | 9720 psi | ASTM D638 | |
| Elongation at Break | 8.3 % | 8.3 % | ASTM D638 |
| 12.6 % | 12.6 % | ISO 527 | |
| Elongation at Yield | 4.3 % | 4.3 % | ISO 527 |
| 4.6 % | 4.6 % | ASTM D638 | |
| Tensile Modulus | 2.75 GPa | 399 ksi | 50 mm/min; ASTM D638 |
| 2.80 GPa | 406 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 101 MPa | 14600 psi | ASTM D790 |
| 108 MPa | 15700 psi | ISO 178 | |
| Flexural Modulus | 3.10 GPa | 450 ksi | ISO 178 |
| 3.23 GPa | 468 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 23.54 J/cm | 44.10 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 137 kJ/m² | 65.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 25.0 J | 18.4 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 34.0 J | 25.1 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 120 °C @Thickness 3.20 mm |
248 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 0.500 mm |
V-0 @Thickness 0.0197 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1e+05 - 1.00e+9 ohm | 1e+05 - 1.00e+9 ohm | ASTM D257 |