SABIC Innovative Plastics LNP STAT-KON DX05301C PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON DX05301C PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STAT-KON* DX05301C is a compound based on Polycarbonate containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive, Low Ionic, Low Outgassing, Low LPC and ESD safe. Suitable for Semiconductor and Hard Disk Drive (HDD) Applications.
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
ASTM D792
Density 1.22 g/cc
0.0441 lb/in³
ISO 1183
Melt Flow 22.6 g/10 min

@Load 5.00 kg,
Temperature 300 °C
22.6 g/10 min

@Load 11.0 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 22 g/10 min

@Load 5.00 kg,
Temperature 300 °C
22 g/10 min

@Load 11.0 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 56.0 MPa
8120 psi
5 mm/min; ISO 527
60.0 MPa
8700 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 48.0 MPa
6960 psi
Type I, 5 mm/min; ASTM D638
56.0 MPa
8120 psi
5 mm/min; ISO 527
Elongation at Break 1.5 %
1.5 %
5 mm/min; ISO 527
9.9 %
9.9 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 1.5 %
1.5 %
5 mm/min; ISO 527
5.3 %
5.3 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 2.49 GPa
361 ksi
1 mm/min; ISO 527
2.59 GPa
376 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 77.0 MPa
11200 psi
2 mm/min; ISO 178
95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.28 GPa
331 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.48 GPa
360 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.540 J/cm
1.01 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 51.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
28.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 52.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
28.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 131 °C
268 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
132 °C

@Thickness 3.20 mm
270 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 146 °C
295 °F
Rate B/120; ISO 306
Electrical Properties Metric English Comments
Volume Resistivity 220000 - 5.50e+8 ohm-cm
220000 - 5.50e+8 ohm-cm
ASTM D257
Surface Resistance 250000 - 4.50e+8 ohm
250000 - 4.50e+8 ohm
ASTM D257