SABIC Innovative Plastics LNP STAT-KON DX04522C PC (Asia Pacific)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP STAT-KON
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP STAT-KON DX04522C PC (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP Stat-Kon DX04522C is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: High Modulus, Electrically Conductive, Clean Compound System. Also known as Stat-Kon PDX-D-04522 CCS.

Physical Properties	Metric	English	Comments
Density	1.365 g/cc	0.04931 lb/inÂ³	ASTM D792
Linear Mold Shrinkage, Flow	0.00060 cm/cm @Time 86400 sec	0.00060 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	135 MPa	19600 psi	Type I, 5 mm/min; ASTM D638
Flexural Strength	114 MPa	16500 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	26.5 GPa	3840 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	0.670 J/cm	1.26 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	136 Â°C @Thickness 3.20 mm	277 Â°F @Thickness 0.126 in	unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Surface Resistance	100 ohm	100 ohm	ASTM D257