SABIC Innovative Plastics LNP STAT-KON DE003P PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DE003P PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DE003P is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| 0.400 % | 0.400 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.00040 - 0.0010 cm/cm @Time 86400 sec |
0.00040 - 0.0010 in/in @Time 24.0 hour |
ASTM D955 |
| 0.00040 - 0.0013 cm/cm @Time 86400 sec |
0.00040 - 0.0013 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0040 cm/cm @Time 86400 sec |
0.0030 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0032 - 0.0041 cm/cm @Time 86400 sec |
0.0032 - 0.0041 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527 |
| 121 MPa | 17500 psi | ASTM D638 | |
| Elongation at Break | 1.4 % | 1.4 % | ISO 527 |
| 1.7 % | 1.7 % | ASTM D638 | |
| Tensile Modulus | 9.88 GPa | 1430 ksi | 1 mm/min; ISO 527 |
| 11.16 GPa | 1619 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 184 MPa | 26700 psi | ISO 178 |
| 193 MPa | 28000 psi | ASTM D790 | |
| Flexural Modulus | 9.77 GPa | 1420 ksi | ISO 178 |
| 9.92 GPa | 1440 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.770 J/cm | 1.44 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.25 J/cm | 7.96 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 16.0 J | 11.8 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 12.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
6.94 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 22.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 49.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 49.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 142 °C | 288 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |