SABIC Innovative Plastics LNP STAT-KON DE0021E PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DE0021E PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DE0021E is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Easy Molding, Flame Retardant, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 |
| 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00060 - 0.0032 cm/cm @Time 86400 sec |
0.00060 - 0.0032 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0029 - 0.0043 cm/cm @Time 86400 sec |
0.0029 - 0.0043 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 112 MPa | 16200 psi | ISO 527 |
| 114 MPa | 16500 psi | ASTM D638 | |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D638 |
| 2.1 % | 2.1 % | ISO 527 | |
| Tensile Modulus | 9.16 GPa | 1330 ksi | 50 mm/min; ASTM D638 |
| 9.36 GPa | 1360 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 169 MPa | 24500 psi | ISO 178 |
| 170 MPa | 24700 psi | ASTM D790 | |
| Flexural Modulus | 8.21 GPa | 1190 ksi | ASTM D790 |
| 8.50 GPa | 1230 ksi | ISO 178 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.47 J/cm | 6.50 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 31.0 kJ/m² | 14.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J | 6.64 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 7.00 J | 5.16 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
9.28 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 16.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
9.28 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 60.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 60.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 93.0 °C @Thickness 3.20 mm |
199 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |