SABIC Innovative Plastics LNP STAT-KON DD0009XP PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DD0009XP PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* DD0009XP is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include:Electrically Conductive, Flame Retardant. Also known as Stat-Kon* D- FR.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.180 % | 0.180 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 54.0 MPa | 7830 psi | Type I, 5 mm/min; ASTM D638 |
| 57.0 MPa | 8270 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 5 mm/min; ASTM D638 |
| 62.0 MPa | 8990 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 5.6 % | 5.6 % | Type I, 5 mm/min; ASTM D638 |
| 7.5 % | 7.5 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 1.2 % | 1.2 % | Type I, 5 mm/min; ASTM D638 |
| 4.2 % | 4.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.81 GPa | 408 ksi | 1 mm/min; ISO 527 |
| 2.82 GPa | 409 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 102 MPa | 14800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.82 GPa | 409 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.88 GPa | 418 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 15.49 J/cm | 29.02 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² | 33.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J | 8.11 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 6.00 J | 4.43 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 53.6 µm/m-°C @Temperature 23.0 - 60.0 °C |
29.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 32.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 56.7 µm/m-°C @Temperature 23.0 - 60.0 °C |
31.5 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 131 °C | 268 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 133 °C @Thickness 3.20 mm |
271 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.70 mm |
V-0 @Thickness 0.0669 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1e+05 - 1.00e+10 ohm | 1e+05 - 1.00e+10 ohm | ASTM D257 |