SABIC Innovative Plastics LNP STAT-KON DD0009P PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON DD0009P PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP STAT-KON* DD0009P is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive.
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
ASTM D792
Moisture Absorption 0.130 %
0.130 %
50% RH, 24 hrs; ASTM D570
0.230 %
0.230 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0078 cm/cm

@Time 86400 sec
0.0078 in/in

@Time 24.0 hour
ISO 294
0.0080 cm/cm

@Time 86400 sec
0.0080 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0080 cm/cm

@Time 86400 sec
0.0080 in/in

@Time 24.0 hour
ASTM D955
0.0080 cm/cm

@Time 86400 sec
0.0080 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.0 MPa
7690 psi
ISO 527
54.0 MPa
7830 psi
ASTM D638
Tensile Strength, Yield 59.0 MPa
8560 psi
ISO 527
64.0 MPa
9280 psi
ASTM D638
Elongation at Break 9.5 %
9.5 %
ISO 527
10 %
10 %
ASTM D638
Elongation at Yield 4.4 %
4.4 %
ISO 527
4.8 %
4.8 %
ASTM D638
Tensile Modulus 2.62 GPa
380 ksi
50 mm/min; ASTM D638
2.80 GPa
406 ksi
1 mm/min; ISO 527
Flexural Strength 102 MPa
14800 psi
ASTM D790
102 MPa
14800 psi
ISO 178
Flexural Modulus 2.82 GPa
409 ksi
ASTM D790
3.00 GPa
435 ksi
ISO 178
Izod Impact, Notched 1.14 J/cm
2.14 ft-lb/in
ASTM D256
Izod Impact, Unnotched 20.93 J/cm
39.21 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 134 kJ/m²
63.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 12.0 J
8.85 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 35.0 J
25.8 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 140 °C

@Thickness 3.20 mm
284 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 128 °C
262 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
130 °C

@Thickness 3.20 mm
266 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 V-1

@Thickness 1.50 mm
V-1

@Thickness 0.0591 in
UL 94 by SABIC-IP
Electrical Properties Metric English Comments
Surface Resistance 100 - 1.00e+6 ohm
100 - 1.00e+6 ohm
ASTM D257