SABIC Innovative Plastics LNP STAT-KON CX99000 PS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON CX99000 PS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* CX99000 is a compound based on Polystyrene containing Carbon Powder. Added features include : Electrically Conductive, Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm | 0.0080 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 23.0 MPa | 3340 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.2 % | 2.2 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 1.70 GPa | 247 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 41.0 MPa | 5950 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.70 GPa | 247 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10000 - 1.00e+6 ohm | 10000 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C1200HF PC+ABS (Europe-Africa-Middle East)
- LG Chemical LUPOL GP2100 PP+GF10%
- Meehanite GM-60 Flake Graphite Cast Iron
- Sylvin Technologies 8925-75 Natural PVC Extrusion Compound
- A. Schulman POLYPUR™ FPU 1185 Thermoplastic Polyurethane Compound
- Westlake Epolene® E-25 Chemically Modified Polypropylene, Maleation Processed
- A. Schulman POLYBATCH™ Red 5670 Concentrate Based In Polyethylene
- DuPont Performance Polymers Delrin® 327UVE RD402 Acetal (POM) (Unverified Data**)
- Polimeri Europa EDISTIR SRL550 High Impact Polystyrene (HIPS) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved