SABIC Innovative Plastics LNP STAT-KON 9X08403C Liquid Crystal Polymer (LCP)

Category Polymer , Thermoplastic , Liquid Crystal Polymer (LCP)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON 9X08403C Liquid Crystal Polymer (LCP).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STAT-KON* 9X08403C is a compound based on Liquid Crystal Polymer (LCP) resin containing Carbon Fiber. Added features of this material are: Clean Compounding System, High Temperature, Flame Retardant, Electrically Conductive, Good barrier against water and oxygen.
Physical Properties Metric English Comments
Specific Gravity 1.46 g/cc
1.46 g/cc
ASTM D792
Density 1.46 g/cc
0.0527 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0052 cm/cm
0.0052 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 153 MPa
22200 psi
Type I, 5 mm/min; ASTM D638
Elongation at Yield 2.7 %
2.7 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 14.8 GPa
2150 ksi
5 mm/min; ASTM D638
Flexural Strength 53.0 MPa
7690 psi
ASTM D790
Flexural Modulus 14.4 GPa
2090 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.870 J/cm
1.63 ft-lb/in
ASTM D256
Izod Impact, Unnotched 8.26 J/cm
15.5 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 280 °C

@Thickness 3.20 mm
536 °F

@Thickness 0.126 in
unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 1e+05 - 1.00e+9 ohm-cm
1e+05 - 1.00e+9 ohm-cm
ASTM D257
Surface Resistance 1e+05 - 1.00e+9 ohm
1e+05 - 1.00e+9 ohm
ASTM D257