SABIC Innovative Plastics LNP Lubriloy D20001 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubriloy D20001 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRILOY* D20001 is a compound based on Polycarbonate resin containing Flame Retardant, Proprietary Lubricant. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D 792 |
| 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.12 % | 0.12 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0053 cm/cm @Time 86400 sec |
0.0053 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0057 cm/cm @Time 86400 sec |
0.0057 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 54.0 MPa | 7830 psi | ISO 527 |
| 60.0 MPa | 8700 psi | ASTM D 638 | |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | ISO 527 |
| 67.0 MPa | 9720 psi | ASTM D 638 | |
| Elongation at Break | 6.5 % | 6.5 % | ASTM D 638 |
| 6.7 % | 6.7 % | ISO 527 | |
| Elongation at Yield | 4.3 % | 4.3 % | ISO 527 |
| 4.5 % | 4.5 % | ASTM D 638 | |
| Tensile Modulus | 2.55 GPa | 370 ksi | 50 mm/min; ASTM D 638 |
| 2.60 GPa | 377 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 102 MPa | 14800 psi | ISO 178 |
| 103 MPa | 14900 psi | ASTM D 790 | |
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO 178 |
| 2.82 GPa | 409 ksi | ASTM D 790 | |
| Izod Impact, Notched | 0.640 J/cm @Temperature 23.0 °C |
1.20 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 16.12 J/cm @Temperature 23.0 °C |
30.20 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 104 kJ/m² @Temperature 23.0 °C |
49.5 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 51.0 J @Temperature 23.0 °C |
37.6 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Coefficient of Friction, Dynamic | 0.090 | 0.090 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.22 | 0.22 | ASTM D 3702 Modified |
| K (wear) Factor | 60.4 x 10-8 mm³/N-M | 30.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.5 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 65.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.5 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 66.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 66.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 89.0 °C @Thickness 3.20 mm |
192 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |