SABIC Innovative Plastics LNP Lubricomp ZFL34 PPO

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp ZFL34 PPO.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* ZFL34 is a compound based on Modified PPO containing glass fiber and PTFE.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.32 g/cc
1.32 g/cc
ASTM D 792
Density 1.32 g/cc
0.0477 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.070 %
0.070 %
23°C / 50% RH; ISO 62
0.060 %

@Time 86400 sec
0.060 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Time 86400 sec
0.0040 - 0.0060 in/in

@Time 24.0 hour
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 91.0 MPa
13200 psi
5 mm/min; ISO 527
96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 91.0 MPa
13200 psi
5 mm/min; ISO 527
96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 1.8 %
1.8 %
5 mm/min; ISO 527
2.7 %
2.7 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 1.8 %
1.8 %
5 mm/min; ISO 527
1.9 %
1.9 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 6.81 GPa
988 ksi
1 mm/min; ISO 527
7.21 GPa
1050 ksi
50 mm/min; ASTM D 638
Flexural Strength 135 MPa
19600 psi
1.3 mm/min, 50 mm span; ASTM D 790
136 MPa
19700 psi
ISO 178
136 MPa
19700 psi
2 mm/min; ISO 178
Flexural Yield Strength 135 MPa
19600 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 6.43 GPa
933 ksi
2 mm/min; ISO 178
6.79 GPa
985 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.990 J/cm

@Temperature 23.0 °C
1.85 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 5.16 J/cm

@Temperature 23.0 °C
9.67 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 30.0 kJ/m²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
12.0 J

@Temperature 23.0 °C
8.85 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Coefficient of Friction, Dynamic 0.44
0.44
ASTM D 3702 Modified
Coefficient of Friction, Static 0.59
0.59
ASTM D 3702 Modified
K (wear) Factor 187 x 10-8 mm³/N-M
93.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 61.4 µm/m-°C

@Temperature -30.0 - 30.0 °C
34.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D 696
CTE, linear, Transverse to Flow 45.6 µm/m-°C

@Temperature -30.0 - 30.0 °C
25.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 139 °C
282 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
138 °C

@Thickness 3.20 mm
280 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 133 °C
271 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
133 °C

@Thickness 3.20 mm
271 °F

@Thickness 0.126 in
unannealed; ASTM D 648