SABIC Innovative Plastics LNP Lubricomp XL004 Amorphous Polyamide
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp XL004 Amorphous Polyamide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* XL-4040 is a compound based on Amorphous Nylon, containing PTFE.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D 792 |
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.44 % | 0.44 % | 23°C / 50% RH; ISO 62 |
| 0.32 % @Time 86400 sec |
0.32 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D 638 |
| 59.0 MPa | 8560 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 5.00 MPa | 725 psi | 50 mm/min; ISO 527 |
| 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 3.9 % | 3.9 % | Type I, 5 mm/min; ASTM D 638 |
| 9.5 % | 9.5 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.9 % | 3.9 % | Type I, 5 mm/min; ASTM D 638 |
| 5.9 % | 5.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.64 GPa | 383 ksi | 1 mm/min; ISO 527 |
| 2.74 GPa | 397 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 88.0 MPa | 12800 psi | ISO 178 |
| Flexural Modulus | 2.31 GPa | 335 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 2.60 GPa | 377 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.300 J/cm @Temperature 23.0 °C |
0.562 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 6.97 J/cm @Temperature 23.0 °C |
13.1 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 46.0 kJ/m² @Temperature 23.0 °C |
21.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.14 | 0.14 | ASTM D 3702 Modified |
| K (wear) Factor | 22.2 x 10-8 mm³/N-M | 11.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 69.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
38.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
40.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 136 °C | 277 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 131 °C @Thickness 3.20 mm |
268 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 120 °C @Thickness 3.20 mm |
248 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |