SABIC Innovative Plastics LNP Lubricomp SX93441D PA6.12

Category Polymer , Thermoplastic , Nylon , Nylon 612
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp SX93441D PA6.12.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* SX93441D is a compound based on Nylon 6/12 containing Proprietary Fillers. Characteristics of this grade are: Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Density 1.19 g/cc
0.0430 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C / 50% RH; ISO 62
0.15 %

@Time 86400 sec
0.15 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0030 - 0.0060 cm/cm

@Time 86400 sec
0.0030 - 0.0060 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.0090 - 0.020 cm/cm

@Time 86400 sec
0.0090 - 0.020 in/in

@Time 24.0 hour
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 86.0 MPa
12500 psi
Type I, 5 mm/min; ASTM D 638
91.0 MPa
13200 psi
5 mm/min; ISO 527
Tensile Strength, Yield 92.0 MPa
13300 psi
5 mm/min; ISO 527
93.0 MPa
13500 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 6.1 %
6.1 %
Type I, 5 mm/min; ASTM D 638
6.3 %
6.3 %
5 mm/min; ISO 527
Elongation at Yield 4.9 %
4.9 %
Type I, 5 mm/min; ASTM D 638
4.9 %
4.9 %
5 mm/min; ISO 527
Tensile Modulus 5.41 GPa
785 ksi
50 mm/min; ASTM D 638
5.41 GPa
785 ksi
1 mm/min; ISO 527
Flexural Strength 136 MPa
19700 psi
ISO 178
Flexural Modulus 4.48 GPa
650 ksi
1.3 mm/min, 50 mm span; ASTM D 790
4.72 GPa
685 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.27 J/cm

@Temperature 23.0 °C
2.38 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 8.70 J/cm

@Temperature 23.0 °C
16.3 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 58.0 kJ/m²

@Temperature 23.0 °C
27.6 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
16.0 J

@Temperature 23.0 °C
11.8 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Coefficient of Friction, Dynamic 0.48
0.48
ASTM D 3702 Modified
Coefficient of Friction, Static 0.47
0.47
ASTM D 3702 Modified
K (wear) Factor 14.1 x 10-8 mm³/N-M
7.00 x 10-10 in³-min/ft-lb-hr
Ring; ASTM D 3702 Modified
103 x 10-8 mm³/N-M
51.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
22.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 170 °C
338 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
175 °C

@Thickness 3.20 mm
347 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 146 °C
295 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
161 °C

@Thickness 3.20 mm
322 °F

@Thickness 0.126 in
unannealed; ASTM D 648