SABIC Innovative Plastics LNP Lubricomp QCL329 PA 6/10 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp QCL329 PA 6/10 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* QCL329 is a compound based on Nylon 6/10 resin containing Carbon Fiber, PTFE, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| 1.44 g/cc | 0.0520 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.19 % | 0.19 % | 23°C / 50% RH; ISO 62 |
| 0.13 % @Time 86400 sec |
0.13 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D 638 |
| 126 MPa | 18300 psi | ISO 527 | |
| Elongation at Break | 2.4 % | 2.4 % | ISO 527 |
| 2.5 % | 2.5 % | ASTM D 638 | |
| Tensile Modulus | 8.82 GPa | 1280 ksi | 50 mm/min; ASTM D 638 |
| 9.58 GPa | 1390 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 171 MPa | 24800 psi | ASTM D 790 |
| 185 MPa | 26800 psi | ISO 178 | |
| Flexural Modulus | 5.99 GPa | 869 ksi | ASTM D 790 |
| 7.01 GPa | 1020 ksi | ISO 178 | |
| Izod Impact, Notched | 0.370 J/cm @Temperature 23.0 °C |
0.693 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 3.79 J/cm @Temperature 23.0 °C |
7.10 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² @Temperature 23.0 °C |
13.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 9.00 J | 6.64 ft-lb | Multiaxial Impact; ISO 6603 |
| 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Coefficient of Friction, Dynamic | 0.47 | 0.47 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.37 | 0.37 | ASTM D 3702 Modified |
| K (wear) Factor | 127 x 10-8 mm³/N-M | 63.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 164 °C @Thickness 3.20 mm |
327 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 ohm-cm - 1e+05 | 1000 ohm-cm - 1e+05 | ASTM D 257 |
| Surface Resistance | 1000 ohm - 1e+05 | 1000 ohm - 1e+05 | ASTM D 257 |