SABIC Innovative Plastics LNP Lubricomp PL004 PA 6

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp PL004 PA 6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* PL004 is a compound based on Nylon 6 containing PTFE Lubricant. Characteristics of this grade are Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.25 g/cc
1.25 g/cc
ASTM D 792
Density 1.25 g/cc
0.0452 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 1.8 %
1.8 %
23°C / 50% RH; ISO 62
1.1 %

@Time 86400 sec
 1.1 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.010 - 0.030 cm/cm

@Time 86400 sec
 0.010 - 0.030 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
 0.010 - 0.030 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 51.0 MPa
7400 psi
Type I, 5 mm/min; ASTM D 638
59.0 MPa
8560 psi
5 mm/min; ISO 527
Tensile Strength, Yield 59.0 MPa
8560 psi
Type I, 5 mm/min; ASTM D 638
61.0 MPa
8850 psi
5 mm/min; ISO 527
Elongation at Break 15.4 %
15.4 %
5 mm/min; ISO 527
31 %
31 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 3.9 %
3.9 %
Type I, 5 mm/min; ASTM D 638
4.0 %
4.0 %
5 mm/min; ISO 527
Tensile Modulus 2.71 GPa
393 ksi
50 mm/min; ASTM D 638
2.85 GPa
413 ksi
1 mm/min; ISO 527
Flexural Strength 90.0 MPa
13100 psi
ISO 178
Flexural Modulus 2.47 GPa
358 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.54 GPa
368 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.520 J/cm

@Temperature 23.0 °C
 0.974 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 13.5 J/cm

@Temperature 23.0 °C
 25.3 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 96.0 kJ/m²

@Temperature 23.0 °C
 45.7 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
5.00 J

@Temperature 23.0 °C
 3.69 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Coefficient of Friction, Dynamic 0.26
0.26
ASTM D 3702 Modified
Coefficient of Friction, Static 0.31
0.31
ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 117 µm/m-°C

@Temperature -30.0 - 30.0 °C
 65.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 123 µm/m-°C

@Temperature -30.0 - 30.0 °C
 68.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
181 °C

@Thickness 3.20 mm
 358 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 52.0 °C
126 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
53.0 °C

@Thickness 3.20 mm
 127 °F

@Thickness 0.126 in
 unannealed; ASTM D 648