SABIC Innovative Plastics LNP Lubricomp OFB32I PPS

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp OFB32I PPS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* OFB32I is a compound based on Polyphenylene Sulfide resin containing Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.55 g/cc
0.0560 lb/in³
ASTM D 792
1.55 g/cc
0.0560 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.020 %
0.020 %
23°C / 50% RH; ISO 62
0.020 %

@Time 86400 sec
0.020 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.00060 cm/cm

@Time 86400 sec
0.00060 in/in

@Time 24.0 hour
ISO 294
0.0010 cm/cm

@Time 86400 sec
0.0010 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.0040 cm/cm

@Time 86400 sec
0.0040 in/in

@Time 24.0 hour
ASTM D 955
0.0044 cm/cm

@Time 86400 sec
0.0044 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 121 MPa
17500 psi
ASTM D 638
165 MPa
23900 psi
ISO 527
Elongation at Break 0.80 %
0.80 %
ASTM D 638
0.80 %
0.80 %
ISO 527
Tensile Modulus 22.95 GPa
3329 ksi
50 mm/min; ASTM D 638
26.2 GPa
3800 ksi
1 mm/min; ISO 527
Flexural Strength 253 MPa
36700 psi
ASTM D 790
259 MPa
37600 psi
ISO 178
Flexural Modulus 24.54 GPa
3559 ksi
ASTM D 790
25.94 GPa
3762 ksi
ISO 178
Izod Impact, Notched 0.480 J/cm

@Temperature 23.0 °C
0.899 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 3.95 J/cm

@Temperature 23.0 °C
7.40 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 24.0 kJ/m²

@Temperature 23.0 °C
11.4 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
4.00 J

@Temperature 23.0 °C
2.95 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Coefficient of Friction, Dynamic 0.36
0.36
ASTM D 3702 Modified
Coefficient of Friction, Static 0.31
0.31
ASTM D 3702 Modified
K (wear) Factor 94.7 x 10-8 mm³/N-M
47.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 265 °C
509 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
269 °C

@Thickness 3.20 mm
516 °F

@Thickness 0.126 in
unannealed; ASTM D 648