SABIC Innovative Plastics LNP Lubricomp JX91055 PES (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP Lubricomp JX91055 PES (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* LUBRICOMP* JX91055 is a compound based on Polyethersulfone resin containing Carbon Fiber and Proprietary Lubricant . Added features include Internally Lubricated and Electrically Conductive.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.

Physical Properties	Metric	English	Comments
Density	1.50 g/cc	0.0542 lb/inÂ³	ISO 1183
Linear Mold Shrinkage, Flow	0.0020 cm/cm	0.0020 in/in	SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	112 MPa	16200 psi	5 mm/min; ISO 527
Elongation at Break	1.4 %	1.4 %	5 mm/min; ISO 527
Tensile Modulus	10.5 GPa	1520 ksi	1 mm/min; ISO 527
Flexural Strength	152 MPa	22000 psi	2 mm/min; ISO 178
Flexural Yield Strength	153 MPa	22200 psi	2 mm/min; ISO 178
Flexural Modulus	8.10 GPa	1170 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	6.00 kJ/mÂ² @Temperature 23.0 Â°C	2.86 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	20.0 kJ/mÂ² @Temperature 23.0 Â°C	9.52 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	227 Â°C	441 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi)	222 Â°C	432 Â°F	Flatw 80104 sp=64mm; ISO 75/Af

Electrical Properties	Metric	English	Comments
Surface Resistance	100 ohm - 1e+05	100 ohm - 1e+05	ASTM D 257