Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp JL003 PES.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* JL003 is a compound based on Polyethersulfone resin containing PTFE.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.45 g/cc
1.45 g/cc
ASTM D 792
Density 1.45 g/cc
0.0524 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.79 %
0.79 %
23°C / 50% RH; ISO 62
0.47 %

@Time 86400 sec
0.47 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0080 - 0.010 cm/cm

@Time 86400 sec
0.0080 - 0.010 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
0.010 - 0.030 in/in

@Time 24.0 hour
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.0 MPa
7690 psi
5 mm/min; ISO 527
54.0 MPa
7830 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 60.0 MPa
8700 psi
5 mm/min; ISO 527
62.0 MPa
8990 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 10.3 %
10.3 %
Type I, 5 mm/min; ASTM D 638
11.2 %
11.2 %
5 mm/min; ISO 527
Elongation at Yield 5.9 %
5.9 %
Type I, 5 mm/min; ASTM D 638
5.9 %
5.9 %
5 mm/min; ISO 527
Tensile Modulus 2.16 GPa
313 ksi
1 mm/min; ISO 527
2.25 GPa
326 ksi
50 mm/min; ASTM D 638
Flexural Strength 80.0 MPa
11600 psi
ISO 178
Flexural Modulus 2.21 GPa
321 ksi
2 mm/min; ISO 178
2.34 GPa
339 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.560 J/cm

@Temperature 23.0 °C
1.05 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 10.6 J/cm

@Temperature 23.0 °C
19.9 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Unnotched (ISO) 68.0 kJ/m²

@Temperature 23.0 °C
32.4 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
6.00 J

@Temperature 23.0 °C
4.43 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Coefficient of Friction, Dynamic 0.23
0.23
ASTM D 3702 Modified
Coefficient of Friction, Static 0.12
0.12
ASTM D 3702 Modified
K (wear) Factor 46.3 x 10-8 mm³/N-M
23.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 214 °C
417 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
218 °C

@Thickness 3.20 mm
424 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 199 °C
390 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
203 °C

@Thickness 3.20 mm
397 °F

@Thickness 0.126 in
unannealed; ASTM D 648