Material Notes:
LNP* Lubricomp* DP0039 is a Polycarbonate base resin containing PTFE and Silicone lubricants. Characteristics are: Flame Retardant.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
ISO 1183
1.30 g/cc
0.0470 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.19 %
0.19 %
23°C / 50% RH; ISO 62
0.12 %

@Time 86400 sec
 0.12 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Time 86400 sec
 0.0050 - 0.0070 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.0070 - 0.0090 cm/cm

@Time 86400 sec
 0.0070 - 0.0090 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 43.0 MPa
6240 psi
5 mm/min; ISO 527
46.0 MPa
6670 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 51.0 MPa
7400 psi
5 mm/min; ISO 527
53.0 MPa
7690 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 23.3 %
23.3 %
5 mm/min; ISO 527
36.8 %
36.8 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 5.4 %
5.4 %
5 mm/min; ISO 527
53.6 %
53.6 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 2.14 GPa
310 ksi
1 mm/min; ISO 527
2.29 GPa
332 ksi
50 mm/min; ASTM D 638
Flexural Strength 69.0 MPa
10000 psi
ISO 178
82.0 MPa
11900 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Yield Strength 84.0 MPa
12200 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.12 GPa
307 ksi
2 mm/min; ISO 178
2.32 GPa
336 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 2.92 J/cm

@Temperature 23.0 °C
 5.47 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 16.7 J/cm

@Temperature 23.0 °C
 31.3 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 23.0 kJ/m²

@Temperature 23.0 °C
 10.9 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 175 kJ/m²

@Temperature 23.0 °C
 83.3 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 20.0 J
14.8 ft-lb
Multiaxial Impact; ISO 6603
33.0 J

@Temperature 23.0 °C
 24.3 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Coefficient of Friction, Dynamic 0.26
0.26
ASTM D 3702 Modified
Coefficient of Friction, Static 0.11
0.11
ASTM D 3702 Modified
K (wear) Factor 90.6 x 10-8 mm³/N-M
45.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 38.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 38.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 135 °C
275 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
136 °C

@Thickness 3.20 mm
 277 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 122 °C
252 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
122 °C

@Thickness 3.20 mm
 252 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Flammability, UL94 V-0

@Thickness 1.70 mm
 V-0

@Thickness 0.0669 in
 UL 94 by SABIC-IP