SABIC Innovative Plastics LNP Lubricomp DFP22 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp DFP22 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* DFP22 is a Polycarbonate base resin containing glass fiber and PTFE/Silicone Lubricants. Characteristic of this grade is: Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 |
| 1.33 g/cc | 0.0480 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.18 % | 0.18 % | 23°C / 50% RH; ISO 62 |
| 0.11 % @Time 86400 sec |
0.11 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | Type I, 5 mm/min; ASTM D 638 |
| 71.0 MPa | 10300 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 73.0 MPa | 10600 psi | Type I, 5 mm/min; ASTM D 638 |
| 73.0 MPa | 10600 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 4.3 % | 4.3 % | 5 mm/min; ISO 527 |
| 4.9 % | 4.9 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 3.4 % | 3.4 % | Type I, 5 mm/min; ASTM D 638 |
| 3.4 % | 3.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.18 GPa | 606 ksi | 1 mm/min; ISO 527 |
| 4.45 GPa | 645 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 122 MPa | 17700 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 3.95 GPa | 573 ksi | 2 mm/min; ISO 178 |
| 4.08 GPa | 592 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 1.72 J/cm @Temperature 23.0 °C |
3.22 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 8.11 J/cm @Temperature 23.0 °C |
15.2 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 7.00 J | 5.16 ft-lb | Multiaxial Impact; ISO 6603 |
| 20.0 J @Temperature 23.0 °C |
14.8 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 | |
| Coefficient of Friction, Dynamic | 0.45 | 0.45 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.52 | 0.52 | ASTM D 3702 Modified |
| K (wear) Factor | 12.1 x 10-8 mm³/N-M | 6.00 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D 3702 Modified |
| 292 x 10-8 mm³/N-M | 145 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 59.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
32.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 57.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
31.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 139 °C @Thickness 3.20 mm |
282 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |