SABIC Innovative Plastics LNP Lubricomp DCL36 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp DCL36 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* DCL36 is a compound based on Polycarbonate resin containing Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
ASTM D 792
Linear Mold Shrinkage, Flow 0.00030 - 0.0010 cm/cm

@Time 86400 sec
0.00030 - 0.0010 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm

@Time 86400 sec
0.0030 - 0.0050 in/in

@Time 24.0 hour
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 158 MPa
22900 psi
ASTM D 638
Elongation at Break 1.7 %
1.7 %
ASTM D 638
Flexural Strength 241 MPa
35000 psi
ASTM D 790
Flexural Modulus 17.92 GPa
2599 ksi
ASTM D 790
Izod Impact, Notched 1.22 J/cm

@Temperature 23.0 °C
2.29 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 5.34 J/cm

@Temperature 23.0 °C
10.0 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Coefficient of Friction, Dynamic 0.43
0.43
ASTM D 3702 Modified
Coefficient of Friction, Static 0.34
0.34
ASTM D 3702 Modified
K (wear) Factor 76.5 x 10-8 mm³/N-M
38.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 145 °C

@Thickness 3.20 mm
293 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Electrical Properties Metric English Comments
Volume Resistivity 10000 ohm-cm - 1e+05
10000 ohm-cm - 1e+05
ASTM D 257
Surface Resistance 1000 - 10000 ohm
1000 - 10000 ohm
ASTM D 257