SABIC Innovative Plastics LNP Lubricomp DCL329XZ PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp DCL329XZ PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* DCL329XZ is a compound based on Polycarbonate resin containing Carbon Fiber, Flame Retardant, PTFE. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
1.365 g/cc
0.04931 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.14 %
0.14 %
23°C / 50% RH; ISO 62
0.090 %

@Time 86400 sec
0.090 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0010 - 0.0020 cm/cm

@Time 86400 sec
0.0010 - 0.0020 in/in

@Time 24.0 hour
ASTM D 955
0.0014 - 0.0019 cm/cm

@Time 86400 sec
0.0014 - 0.0019 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0040 - 0.0050 cm/cm

@Time 86400 sec
0.0040 - 0.0050 in/in

@Time 24.0 hour
ASTM D 955
0.0045 - 0.0052 cm/cm

@Time 86400 sec
0.0045 - 0.0052 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 91.0 MPa
13200 psi
ASTM D 638
94.0 MPa
13600 psi
ISO 527
Elongation at Break 1.9 %
1.9 %
ISO 527
2.0 %
2.0 %
ASTM D 638
Tensile Modulus 7.17 GPa
1040 ksi
50 mm/min; ASTM D 638
7.30 GPa
1060 ksi
1 mm/min; ISO 527
Flexural Strength 138 MPa
20000 psi
ASTM D 790
139 MPa
20200 psi
ISO 178
Flexural Modulus 6.48 GPa
940 ksi
ASTM D 790
7.30 GPa
1060 ksi
ISO 178
Izod Impact, Notched 0.690 J/cm

@Temperature 23.0 °C
1.29 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 3.15 J/cm

@Temperature 23.0 °C
5.90 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 22.0 kJ/m²

@Temperature 23.0 °C
10.5 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
15.0 J

@Temperature 23.0 °C
11.1 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 24.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
13.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
24.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
13.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 41.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
23.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
41.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
23.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 141 °C
286 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
143 °C

@Thickness 3.20 mm
289 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 138 °C
280 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
139 °C

@Thickness 3.20 mm
282 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Electrical Properties Metric English Comments
Surface Resistance 100 - 1.00e+6 ohm
100 - 1.00e+6 ohm
ASTM D 257