SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRILOY* RX99650 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.730 % | 0.730 % | 50% RH, 24 hrs; ASTM D570 |
| 1.12 % | 1.12 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.024 - 0.026 cm/cm @Time 86400 sec |
0.024 - 0.026 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0243 - 0.026 cm/cm @Time 86400 sec |
0.0243 - 0.026 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.024 - 0.026 cm/cm @Time 86400 sec |
0.024 - 0.026 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0243 - 0.026 cm/cm @Time 86400 sec |
0.0243 - 0.026 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ASTM D638 |
| 54.0 MPa | 7830 psi | ISO 527 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527 |
| 59.0 MPa | 8560 psi | ASTM D638 | |
| Elongation at Break | 31 % | 31 % | ASTM D638 |
| 64 % | 64 % | ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| 16 % | 16 % | ISO 527 | |
| Tensile Modulus | 2.16 GPa | 313 ksi | 1 mm/min; ISO 527 |
| 2.22 GPa | 322 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
| 80.0 MPa | 11600 psi | ASTM D790 | |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| 2.08 GPa | 302 ksi | ASTM D790 | |
| Izod Impact, Notched | 4.27 J/cm | 8.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 137 kJ/m² | 65.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 76.0 J | 56.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 65.0 J | 47.9 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.31 | 0.31 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.18 | 0.18 | ASTM D3702 Modified |
| K (wear) Factor | 16.1 x 10-8 mm³/N-M | 8.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 121 µm/m-°C @Temperature -40.0 - 40.0 °C |
67.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 121 µm/m-°C @Temperature -40.0 - 40.0 °C |
67.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 112 µm/m-°C @Temperature -40.0 - 40.0 °C |
62.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 113 µm/m-°C @Temperature -40.0 - 40.0 °C |
62.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 188 °C | 370 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 206 °C @Thickness 3.20 mm |
403 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 63.0 °C @Thickness 3.20 mm |
145 °F @Thickness 0.126 in |
unannealed; ASTM D648 |