SABIC Innovative Plastics LNP LUBRILOY RF206H PA 66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY RF206H PA 66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRILOY* RF206H is a compound based on Nylon 66 resin containing Glass Fiber, Lubricants, Proprietary Lubricant. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.350 % | 0.350 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm @Time 86400 sec |
0.0030 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0032 - 0.0044 cm/cm @Time 86400 sec |
0.0032 - 0.0044 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.011 - 0.012 cm/cm @Time 86400 sec |
0.011 - 0.012 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0109 - 0.0124 cm/cm @Time 86400 sec |
0.0109 - 0.0124 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 121 MPa | 17500 psi | ISO 527 |
| 122 MPa | 17700 psi | ASTM D638 | |
| Elongation at Break | 2.6 % | 2.6 % | ASTM D638 |
| 2.7 % | 2.7 % | ISO 527 | |
| Tensile Modulus | 8.20 GPa | 1190 ksi | 1 mm/min; ISO 527 |
| 8.89 GPa | 1290 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 178 MPa | 25800 psi | ASTM D790 |
| 192 MPa | 27800 psi | ISO 178 | |
| Flexural Modulus | 6.82 GPa | 989 ksi | ASTM D790 |
| 8.50 GPa | 1230 ksi | ISO 178 | |
| Izod Impact, Notched | 1.22 J/cm | 2.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.58 J/cm | 14.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 48.0 kJ/m² | 22.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 12.0 J | 8.85 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.62 | 0.62 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.43 | 0.43 | ASTM D3702 Modified |
| K (wear) Factor | 58.4 x 10-8 mm³/N-M | 29.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 36.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.5 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 69.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 69.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C @Thickness 3.20 mm |
496 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 241 °C @Thickness 3.20 mm |
466 °F @Thickness 0.126 in |
unannealed; ASTM D648 |