SABIC Innovative Plastics LNP LUBRILOY DF206XXH PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Lubriloy
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRILOY DF206XXH PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRILOY* DF206XXH is a compound based on Polycarbonate containing 30% Glass Fiber, Proprietary Lubricant. Added features of this grade include: Wear Resistant, Healthcare.
Physical Properties Metric English Comments
Specific Gravity 1.40 g/cc
1.40 g/cc
ASTM D792
Density 1.39 g/cc
0.0502 lb/in³
ASTM D792
Moisture Absorption 0.110 %
0.110 %
50% RH, 24 hrs; ASTM D570
0.160 %
0.160 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Time 86400 sec
0.0040 - 0.0060 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Time 86400 sec
0.0050 - 0.0070 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 112 MPa
16200 psi
Type I, 5 mm/min; ASTM D638
112 MPa
16200 psi
5 mm/min; ISO 527
Elongation at Break 2.6 %
2.6 %
Type I, 5 mm/min; ASTM D638
2.6 %
2.6 %
5 mm/min; ISO 527
Tensile Modulus 8.24 GPa
1200 ksi
1 mm/min; ISO 527
8.72 GPa
1260 ksi
5 mm/min; ASTM D638
Flexural Strength 166 MPa
24100 psi
ISO 178
169 MPa
24500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 174 MPa
25200 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 7.58 GPa
1100 ksi
2 mm/min; ISO 178
7.83 GPa
1140 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.78 J/cm
3.33 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.75 J/cm
14.5 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 17.0 kJ/m²
8.09 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 49.0 kJ/m²
23.3 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 26.0 J

@Temperature 23.0 °C
19.2 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 6.00 J
4.43 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.49
0.49
ASTM D3702 Modified
Coefficient of Friction, Static 0.64
0.64
ASTM D3702 Modified
K (wear) Factor 54.4 x 10-8 mm³/N-M
27.0 x 10-10 in³-min/ft-lb-hr
Ring; ASTM D3702 Modified
494 x 10-8 mm³/N-M
245 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 56.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
31.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 51.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
28.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
146 °C

@Thickness 3.20 mm
295 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 141 °C
286 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
142 °C

@Thickness 3.20 mm
288 °F

@Thickness 0.126 in
unannealed; ASTM D648