SABIC Innovative Plastics LNP LUBRILOY D2000P PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY D2000P PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRILOY* D2000P is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Exceptional Processing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792 |
| 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.130 % | 0.130 % | 50% RH, 24 hrs; ASTM D570 |
| 0.210 % | 0.210 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0084 cm/cm @Time 86400 sec |
0.0084 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0081 cm/cm @Time 86400 sec |
0.0081 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | ASTM D638 |
| 46.0 MPa | 6670 psi | ISO 527 | |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | ISO 527 |
| 56.0 MPa | 8120 psi | ASTM D638 | |
| Elongation at Break | 42.3 % | 42.3 % | ASTM D638 |
| 43.1 % | 43.1 % | ISO 527 | |
| Elongation at Yield | 5.3 % | 5.3 % | ISO 527 |
| 5.9 % | 5.9 % | ASTM D638 | |
| Tensile Modulus | 1.93 GPa | 280 ksi | 50 mm/min; ASTM D638 |
| 2.10 GPa | 305 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 86.0 MPa | 12500 psi | ASTM D790 |
| 86.0 MPa | 12500 psi | ISO 178 | |
| Flexural Modulus | 2.27 GPa | 329 ksi | ASTM D790 |
| 2.30 GPa | 334 ksi | ISO 178 | |
| Izod Impact, Notched | 4.53 J/cm | 8.49 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 137 kJ/m² | 65.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 40.0 J | 29.5 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 43.0 J | 31.7 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.19 | 0.19 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.15 | 0.15 | ASTM D3702 Modified |
| K (wear) Factor | 88.6 x 10-8 mm³/N-M | 44.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 71.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 71.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 72.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 72.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 131 °C | 268 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |